What causes the problem of brittle plastic products?

a mold aspect

(1) If the gate is too small, consider adjusting the gate size or adding an auxiliary gate.

(2) If the runner is too small or improperly configured, it should be balanced as much as possible or the size of the runner should be increased.

(3) Poor mold structure causes abnormal injection cycle.

Two equipment aspects

(1) There are dead corners or obstacles in the barrel, which can easily promote the degradation of the melt.

(2) The plasticizing capacity of the machine is too small, the plastic is not plasticized in the barrel; the plasticizing capacity of the machine is too large, the plastic is heated and sheared for too long in the barrel, the plastic is easy to age, and the product is changed. brittle.

(3) The ejector unit is inclined or unbalanced, and the top sectional area is small or improperly distributed.

Three raw materials

(1) When the raw material is mixed with other impurities or is doped with an inappropriate or excessive amount of a solvent or other additives.

(2) Some plastics, such as aBS, will undergo catalytic cracking reaction with water vapor when heated under damp conditions, causing large strain on the part.

(3) If the number of plastic regenerations is too high or the content of recycled materials is too high, or the heating time in the barrel is too long, the parts will be brittle.

(4) The quality of the plastic itself is not good, for example, the molecular weight distribution is large, and the composition of the non-uniform structure such as the rigid molecular chain is excessively occupied; or it is contaminated by other plastics, the contamination of the bad additive, the pollution of dust impurities, etc. the reason.

Four process aspects

(1) The temperature of the barrel and nozzle is too low, and it is raised. If the material is easily degraded, the temperature of the barrel and nozzle should be increased.

(2) Reduce the pre-plastic back pressure and speed of the screw to make the material slightly loose and reduce the degradation of the plastic due to shearing and overheating.

(3) The mold temperature is too high, the demoulding is difficult; the mold temperature is too low, the plastic is prematurely cooled, the fusion joint is poorly fused, and cracking is easy, especially for high melting point plastics such as polycarbonate.

(4) The cavity core should have a proper draft angle. When the core is difficult to demould, it is necessary to increase the cavity temperature and shorten the cooling time. When the cavity is difficult to remove, reduce the cavity temperature and extend the cooling time.

(5) Minimize the use of metal inserts, brittle hot and cold plastics such as polystyrene, and can not be added to insert molding.

Five product design aspects

(1) The product has sharp corners, notches or portions having a large difference in thickness which are prone to stress cracking.

(2) The product design is too thin or too hollow.

Compact Solar Water Heater is a cost-effective system for residential hot water application. This system is designed according to thermosiphon principle and operating with proportion difference between cold and hot water. The water heated by Vacuum Tubes is held in the stainless steel storage tank where the insulation preserves the heat.

 

The compact Solar Water Heater uses the sun to heat the working fluid (mostly water) in the vacuum tubes. The Solar Collector absorbs solar radiation, and converts the sunlight to heat and transfer it to the water. The heated water naturally rises through the solar collector into the water tank where the cooler water at the bottom of the tank is forced out and descends to the bottom of the collector (thermosiphon circulation). The circulation will be interrupted when there is no solar radiation.


Pressurized Heatpipe Swh

Compact Solar Water Heater

Compact Water Heater,Compact Solar Water Heater,Compact Pressurized Solar Water Heater,Compact Non-Pressurized Solar Water Heater

Linuo Ritter International Co.,Ltd , https://www.lnrtsolarenergy.com

Posted on